Supratec Membrane offers highest-quality ultrafiltration membranes based on PVDF at very competitive prices. Our membranes are characterized by an extremely porous and homogeneous pore structure. These excellent features lead to significant advantages in the operation of MBR applications:
More about technical features: Technical features
| Membrane type | Ultrafiltration Flatsheet Membrane | Ultrafiltration Hollow Fiber Membrane |
|---|---|---|
| Membrane material | PVDF | PVDF |
| Nominal pore size | 0.03 µm | 0.03 µm |
| Maximum pore size | 0.05 µm | 0.05 µm |
| Pure water permeability | >1.500 LMH/bar | >3.000 LMH/bar |
| Membrane Flux (MBR-application) | 10 - 60 l/m²h | 10 - 60 l/m²h |
| Membrane width | 40,0“ | 40,0“ |
| Membrane thickness including backing material | 230µm | 230µm |
| backing material | PET (optional PP) Fleece | PET braid |
| Max cleaning concentration | Max operating concentration | Life time exposure | |
|---|---|---|---|
| Chlorine as Cl at 20°C | 5,000 ppm | 6 ppm | 5,000,000 ppm·h |
| Chlorine as Cl at 40°C | 3,000 ppm | 4 ppm | 3,000,000 ppm·h |
| Acid/Base at up to 40°C | 2 – 11 pH | 5 – 10 pH | 70,000 ppm·h as NaOH |
| Mixture of base and Cl2 | 3,000 ppm Chlorine | n.a. | 3,000,000 ppm·h Chlorine |
| Ozone at 40°C | 0.5 ppm for < 300 h | 0.50 ppm | 200 ppm·h |
| Ozone at 20°C | 0.55 ppm for < 300 h | 0.55 ppm | 250 ppm·h |
| Water oversaturated O2 | n.a. | Oversaturated | No limit |
Conditioning/drying prevention:
Our membranes are impregnated with glycerin or other alternative material to prevent the membrane pores from collapsing during transport and storage. The conditioning material will be washed out before activation and final use. For the operation the membrane has to be activated.
For detailed instructions on washing, activating and conditioning or alternative activation procedures, please contact Supratec Membrane GmbH.